Alloy 25 C17200 Beryllium Copper Strip 0.25mm*9.5mm State 1/2
Hard(TD02)
Product Normal Description:
Product Name: Beryllium copper strip
Grade: Alloy 25 C17200
Product Specification: 0.25mm*9.5mm
State: 1/2 Hard(TD02)
Product Brand: CUBERYLLIUM®
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions.
These fall into two categories: alloys selected for high strength
(Alloys 172,173,170) and alloys selected for high conductivity
(Alloys 751,750,741). Also Supply Master alloy : CuBeryllium-200;
CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global
factory.
Product Data Sheet - C17200 Beryllium Copper Alloy:
C17200 is manufactured to provide a combination of high strength
and hardness properties coupled with superior thermal properties.
This range of properties makes C17200 the premier material for
copper alloy molds and a wide range of other applications from oil
and gas to aerospace.
Chemical Composition (Weight Percent) of C17200 Beryllium Copper Alloy:
| Delivering Solutions |
| Alloy | Beryllium | Cobalt | Nickel | Co + Ni | Co+Ni+Fe | Copper |
| C17200 | 1.80-2.00 | - | 0.20 Min | 0.20 Min | 0.60 Max | Balance |
Remark: Copper plus additions equal 99.5% Min.
Typical Physical Properties of CUBERYLLIUM 172:
Density (g/cm3): 8.36
Density before age hardening (g/cm3): 8.25
Elastic Modulus (kg/mm2 (103)): 13.40
Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): 17 x 10-6
Thermal Conductivity (cal/(cm-s-°C)): 0.25
Melting Range (°C): 870-980
Common Temper we supply:
| CuBeryllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Strip |
| Designation | Description | Tensile Strength
(Mpa) | Yield Strength 0.2% offset | Elongation Percent | HARDNESS
(HV) | HARDNESS
Rockwell
B or C Scale | Electrical Conductivity
(% IACS) |
| A | TB00 | Solution Annealed | 410～530 | 190～380 | 35~60 | <130 | 45~78HRB | 15～19 |
| 1/2 H | TD02 | Half Hard | 580～690 | 510～660 | 12~30 | 180~220 | 88~96HRB | 15～19 |
| H | TD04 | Hard | 680~830 | 620~800 | 2~18 | 220~240 | 96~102HRB | 15～19 |
| HM | TM04 |
Mill hardened | 930～1040 | 750～940 | 9～20 | 270～325 | 28～35HRC | 17～28 |
| SHM | TM05 | 1030～1110 | 860～970 | 9～18 | 295～350 | 31～37HRC | 17～28 |
| XHM | TM06 | 1060～1210 | 930～1180 | 4～15 | 300～360 | 32～38HRC | 17～28 |
Key Technology of Beryllium Copper(Heat treatment)
Heat treatment is the most important process for this alloy system.
While all copper alloys are hardenable by cold working, beryllium
copper is unique in being hardenable by a simple low temperature
thermal treatment. It involves two basic steps. The first is called
solution annealing and the second, precipitation or age hardening.
Solution Annealing
For the typical alloy CuBe1.9 (1.8- 2%) the alloy is heated between
720°C and 860°C. At this point the contained beryllium is
essentially “dissolved” in the copper matrix (alpha phase). By
rapidly quenching to room temperature this solid solution structure
is retained. The material at this stage is very soft and ductile
and can be readily cold worked by drawing, forming rolling, or cold
heading. The solution annealing operation is part of the process at
the mill and is not typically used by the customer. Temperature,
time at temperature, quench rate, grain size, and hardness are all
very critical parameters and are tightly controlled by ohmalloy.
Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.
Size Available
Standard Tolerance
| Tolerance Sheet |
| (MM) |
Strip
Thickness | CuBeryllium®
Standard Tolerance |
| over | incl. | plus or minus |
| 0.03 | 0.08 | 0.003 |
| 0.08 | 0.1 | 0.004 |
| 0.1 | 0.15 | 0.005 |
| 0.15 | 0.2 | 0.006 |
| 0.2 | 0.25 | 0.007 |
| 0.25 | 0.4 | 0.008 |
| 0.4 | 0.55 | 0.009 |
| 0.55 | 0.7 | 0.01 |
| 0.7 | 0.9 | 0.015 |
| 0.9 | 1.5 | 0.025 |
| Note: Tolerances apply to rolled and mill hardened strip. |
Product Photos:
Application
Our alloys combine a range of properties particularly suited to
meet the exacting requirements of many applications in the
automotive, electronic, aeronautical, Oil&Gas, watch,
electro-chemical industries, etc. Beryllium Copper is widely used
in those fields as contact springs in various applications like
connectors, switches, relays, etc
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened
process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06)
XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous
Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the
amount is different.