Nickel Beryllium Copper Pipe European Standard CuNi2Be By Standard
SAE J 461
Product Description:
Name: Nickel beryllium copper pipe
Grade: CuNi2Be (CUBERYLLIUM® 751)
End Product Form: Pipe, Tube
State: A(TB00), H(TD04), AT(TF00), HT(TH04)
Standard: ASTM B 937, SAE J 461, SAE J 463, RWMA Class 3, EN 12163,
EN 12165, EN 12167
Application: Used for industry application
Feature: with highly conductivity
Package: in plywoode cases or wooden cases
Size: Custom Diameter & Sizes, Random Mill Lengths
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions.
These fall into two categories: alloys selected for high strength
(Alloys 172,173,170) and alloys selected for high conductivity
(Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia
Market. Also Supply Master alloy : CuBeryllium-200;
CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global
factory.
Introduction of CuNi2Be (C17510) Copper Alloy:
CuNi2Be—C17510 (CDA 1751) Nickel Beryllium Copper is the mirror
image of alloys C17500 in terms of its properties &
Characteristics. C17510 is also primarily utilized in the industry
applications that require most highly thermal or electrical
conductivity, which features a Nickel alloying addition
(1.40-2.20%). C17510 also offers good strength and hardness
characteristics coupled with conductivity in the range of 45-60
percent of copper with ultimate tensile and hardness properties
approaching 140 ksi and RB 100 respectively.
Chemical Composition of Nickel Beryllium Copper Alloy:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Nickel | Copper |
| Cuberyllium-C751 | C17510 | 0.20~0.60 | 1.4～2.2 | Balance |
Related material specifications of Nickel Beryllium Copper Alloy:
Tubes/Pipes: ASTM B 937, SAE J 461, SAE J 463, RWMA Class 3, EN
12163, EN 12165, EN 12167
European Standards: CuNi2Be, CuNiBe, Alloy 3, DIN. 2.0850, CW110C
to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by
ASTM.
Typical Physical Properties of Nickel Beryllium Copper Alloy:
| Density | 8.83 | g/cm3 |
| Density before age hardening | 8.75 | g/cm3 |
| Elastic Modulus | 14.1 | kg/mm2 (103) |
| Thermal Expansion Coefficient | 18x10-6 | 20 °C to 200 °C m/m/°C |
| Thermal Conductivity | 0.57 | cal/(cm-s-°C) |
| Melting Range | 1000-1070 | °C |
Typical Applications for Nickel Beryllium Copper Alloy:
A: Electrical Industry: Switch Parts, Connectors, Spring
Connectors, Fuse Clips, Relay Parts;
B: Fasteners: Washers, Fasteners;
C: Industrial: Spring, Resistance Welding Equipment, Resistance and
Spot Welding Tips, Seam Welding Dies, Die-Casting Plunger Tips,
Tooling for Plastic Moulds.
Temper Designations of Nickel Beryllium Copper Pipe(CUBERYLLIUM ®-751):
| Cuberyllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Tube/Pipe |
| Temper | Outside Diameter or Distance Between Parallel Surfaces (mm) | Tensile Strength
(Mpa) | Yield Strength 0.2% offset(Mpa) | Elongation Percent | HARDNESS
(Rockwell B Scale) | Electrical Conductiviry percent(IACS) |
| A | TB00 | All sizes | 240～380 | 70～210 | 20-35 | B20-50 | 20-30 |
| H | TD04 | up to 76 | 440~550 | 340~520 | 10-15 | B60-80 | 20-30 |
AT
| TF00 | All sizes | 680～890 | 550～690 | 10-25 | B92-100 | 45-60 |
| HT | TH04 | up to 76 | 750 ~ 960 | 650 ~ 860 | 5-25 | B95-102 | 48-60 |
Product Photo:
Weldability
Soldering, brazing, gas shielded arc welding, coated metal arc
welding, spot welding, seam welding and butt welding are all
recommended
Hot & Cold Workability
Good hot working properties. Excellent cold working properties.
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.
FAQ:
Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous
Furnace.
3:Surface further polishing for top clients.
Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid
before the delivery.
Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the
amount is different.