Beryllium Copper Tube DIN. 2.0850 State A(TB00) H(TD04) AT(TF00)
HT(TH04) For Industry Application
Product Description:
Name: Beryllium Copper Tube
Grade: DIN. 2.0850 (CUBERYLLIUM® 751)
End Product Form: Pipe, Tube
State: A(TB00), H(TD04), AT(TF00), HT(TH04)
Standard: ASTM B 937, SAE J 461, SAE J 463, RWMA Class 3, EN 12163,
EN 12165, EN 12167
Application: Used for industry application
Feature: with highly conductivity
Package: in plywoode cases or wooden cases
Size: Custom Diameter & Sizes, Random Mill Lengths
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions.
These fall into two categories: alloys selected for high strength
(Alloys 172,173,170) and alloys selected for high conductivity
(Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia
Market. Also Supply Master alloy : CuBeryllium-200;
CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global
factory.
CUBERYLLIUM ®-751 also named -C17510 (CDA 1751) combine moderate yield strength, up to 960Mpa(140ksi), with
electrical and thermal conductivity from 45 to 60 % of pure copper.
Alloys 750 and 751 are available in wrought product forms and can
be supplied fully hardened. Hardened products are identified by the
temper designation AT or HT, and have good formability.
Chemical Composition of Beryllium Copper Alloy DIN. 2.0850:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Nickel | Copper |
| Cuberyllium-C751 | C17510 | 0.20~0.60 | 1.4～2.2 | Balance |
Related material specifications of Beryllium Copper Alloy DIN. 2.0850:
Tubes/Pipes: ASTM B 937, SAE J 461, SAE J 463, RWMA Class 3, EN
12163, EN 12165, EN 12167
European Standards: CuNi2Be, CuNiBe, Alloy 3, DIN. 2.0850, CW110C
to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by
ASTM.
Physical Properties
The following table shows the physical properties of UNS C17510
beryllium copper alloys.
| Properties | Metric |
|---|
| Density | 8.83 g/cm3 |
| Density before age hardening | 8.75 g/cm3 |
| Elastic Modulus | 14.1kg/mm2 (103) |
| Thermal Expansion Coefficient | 18x10-6 20 °C to 200 °C m/m/°C |
| Thermal Conductivity | 0.57 cal/(cm-s-°C) |
| Melting Range | 1000-1070 °C |
Typical Applications for Beryllium Copper Alloy DIN. 2.0850:
A: Electrical Industry: Switch Parts, Connectors, Spring
Connectors, Fuse Clips, Relay Parts;
B: Fasteners: Washers, Fasteners;
C: Industrial: Spring, Resistance Welding Equipment, Resistance and
Spot Welding Tips, Seam Welding Dies, Die-Casting Plunger Tips,
Tooling for Plastic Moulds.
Temper Designations of Beryllium Copper Tube DIN. 2.0850(CUBERYLLIUM ®-751):
| Cuberyllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Tube/Pipe |
| Temper | Outside Diameter or Distance Between Parallel Surfaces (mm) | Tensile Strength
(Mpa) | Yield Strength 0.2% offset(Mpa) | Elongation Percent | HARDNESS
(Rockwell B Scale) | Electrical Conductiviry percent(IACS) |
| A | TB00 | All sizes | 240～380 | 70～210 | 20-35 | B20-50 | 20-30 |
| H | TD04 | up to 76 | 440~550 | 340~520 | 10-15 | B60-80 | 20-30 |
AT
| TF00 | All sizes | 680～890 | 550～690 | 10-25 | B92-100 | 45-60 |
| HT | TH04 | up to 76 | 750 ~ 960 | 650 ~ 860 | 5-25 | B95-102 | 48-60 |
Product Photo:
Weldability
Soldering, brazing, gas shielded arc welding, coated metal arc
welding, spot welding, seam welding and butt welding are all
recommended
Hot & Cold Workability
Good hot working properties. Excellent cold working properties.
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.
FAQ:
Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous
Furnace.
3:Surface further polishing for top clients.
Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid
before the delivery.
Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the
amount is different.