BrB2 (CuBe2) Beryllium Copper Plate 6x25x500 TD02 Temper For Oil
Process Platform
Product Normal Description:
Product Name: Beryllum copper plate
Grade: BrB2, CuBe2
Standard: ASTM B194
Product Size: 6mmt x 25mmw x 500mml
State: TD02(1/2H)
Typical Application: For oil process platform
Product Brand: CUBERYLLIUM®
Chemical Composition of BrB2 (CuBe2) Beryllium Copper Alloy:
Product Grade: CUBERYLLIUM ®-172(UNS. C17200)
| Numbering | Be | Co+Ni | Cu | Fe | Pb | Si | Al |
| C17200 | 1.8-2.0 | ≥0.2 | Margin | 0.15 | - | 0.15 | 0.15 |
Note: Copper plus additions equal 99.5% Minimum.
Beryllium Copper Alloys:
Beryllium copper (C17200 & C17300) is an age-hardening alloy which
attains the highest strength of any copper-base alloy. It may be
age-hardened after forming into springs, intricate forms or complex
shapes. It is esteemed for spring properties, erosion obstruction,
soundness, conductivity, and low creep.
Tempered beryllium copper is C17200 and C17300 that has been age
solidified and cold drawn. No further heat treatment is essential
past a potential light pressure alleviation. It is adequately
flexible to twist without anyone else measurement and can be framed
into springs and most shapes. The tempered wire is most valuable
where the properties of beryllium copper are wanted, yet the age
solidifying of completed parts isn’t useful.
C17510 and C17500 beryllium copper alloys are age-hardenable and
give great electrical conductivity, physical properties, and
perseverance. They are utilized in springs and wire where
electrical conduction or maintenance of properties at raised
temperatures is significant.
High-quality beryllium copper combinations contain as much as 2.7%
beryllium (cast), or 1.6-2% beryllium with about 0.3% cobalt
(created).
High conductivity beryllium copper combinations contain as much as
0.7% beryllium with some nickel and cobalt. The thermal
conductivity of these amalgams is more prominent than aluminum and
somewhat not exactly unadulterated copper and are regularly
utilized as electrical contacts.
Typical Physical Properties of BrB2 (CuBe2) Beryllium Copper Alloy:
| Density (g/cm3): | 8.36 |
| Density before age hardening (g/cm3): | 8.25 |
| Elastic Modulus (kg/mm2 (103)): | 13.4 |
| Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
| Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
| Melting Range (°C): | 870-980 |
Temper Designations of BrB2 (CuBe2) Beryllium Copper Plate:
| Mechanical and Electrical Properties of C17200 Sheet/Plate |
| CUBERYLLIUM | ASTM | Heat Treatment | Thickness (mm) | Tensile Strength (Mpa) | Elongation Percent | HARDNESS Rockwell B or C Scale | Electrical Conductivity
(% IACS) |
| Designation | Designation |
| A | TB00 | | All Size | 400~580 | 20~60 | B45-85 | 15～19 |
| H | TD04 | ＜10 | 600~880 | 8~20 | B91-103 | 15～19 |
| 10~25 | 600~850 | 8~20 | B90-102 | 15 ~ 19 |
| 25~50 | 580~820 | 8~20 | B88-102 | 15 ~19 |
| ＞50 | 580~820 | 8~20 | B88-102 | 15 ~19 |
| AT | TF00 |
3 hr 315℃
| All Size | 1120~1358 | 3~10 | C36-41 | 22 ~ 28 |
| HT | TH04 | 2 hr 315℃ | ＜10 | 1200~1450 | 1~5 | C38-45 | 22 ~ 28 |
| 10~25 | 1200~1500 | 1~5 | C38-44 | 22 ~ 28 |
| 25~50 | 1200~1450 | 2~5 | C37-43 | 22 ~ 28 |
| ＞50 | 1100~1350 | 2~5 | C36-42 | 22 ~ 28 |
Product Photos:
Excellent Properties of CuBe2 Copper Alloys:
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.